PLASTIC STRAIN TESTER

Harga : Rp 123.00

Brand : Qualitest,Yasuda Seiki,Toyoseiki,Drick

Stok : In Stock





PLASTIC STRAIN TESTER

COMPRESSION SET TESTER

JIS-A5756, K6262, ASTM-D395, ISO-815

This tester measures the compression set of vulcanized rubber and thermo-plastic rubber at room temperature, low temperature, and high temperature to acquire the settling of the test specimen. The compression ratio can be set by changing the spacer.

Spesifikasi 171 COMPRESSION SET TESTER

Test Method Large Specimen Small Specimen
Test Method φ29.0 ± 0.5 mm
T12.5 ± 0.5 mm
φ13.0 ± 0.5 mm
T6.3 ± 0.3 mm
Spacer 12 pcs, T9.3 to 9.4 mm(25 % Compression)
12 pcs, T4.7 to 4.8 mm(25 % Compression)
Dimensions/ Weight (Approx.) W290 × D150 × H145 (20 × 3 Stages) mm, 20 kg W290 × D150 × H145 (20 × 3 Stages) mm, 20 kg

WILLIAMS PLASTOMETER

JIS-K6249, ASTM-D926, ISO-7323

Placing the specimen on the parallel plate and after adding prescribed load for a specific amount of time, the plastometer reads the thickness of the specimen and multiplies the thickness 100 times to acquire the degree of plasticity.

Spesifikasi

Model No.105
WILLIAMS PLASTOMETER
Specimen Cylindrical shape, Volume 2 ± 0.02 cm3 (φ16 mm, H10 mm)
Parallel Plate Upper: φ148 mm, T12 mm
Lower: φ148 mm, T13 mm
Test Load Initial 24.5 N (2.5 kgf) to Max. 49 ± 0.05 N (5 kgf) (Standard 49 ± 0.05 N)
Dial Gauge Scale 1/100 mm, Stroke Max. 20 mm
Software -
Accessories Dial Gauge, Weight (4.9 N: 1 pc, 9.8 N: 2 pcs), Hexagon wrench,Set Up Disk (105-AUTO), Power Plug Adaptor (105-AUTO)
Option -
Power Source -
Dimensions/Weight (Approx.) W175 × D175 × H330 mm, 10 kg
*With Dial Gauge Attached.

AUTO WILLIAMS PLASTOMETER (AUTOMATIC)

JIS-K6249, ASTM-D926, ISO-7323

The No.105-AUTO is the automated version of the No.105 WILLIAMS PLASTOMETER. The tester can show the time series graph of the thickness on the computer screen.

Spesifikasi

Model No.105-AUTO
WILLIAMS PLASTOMETER (AUTOMATIC)
Specimen Cylindrical shape, Volume 2 ± 0.02 cm3 (φ16 mm, H10 mm)
Parallel Plate Upper: φ148 mm, T12 mm
Lower: φ148 mm, T13 mm
Test Load Initial 24.5 N (2.5 kgf) to Max. 49 ± 0.05 N (5 kgf) (Standard 49 ± 0.05 N)
Dial Gauge Scale 1/100 mm, Stroke Max. 20 mm,Digital Display Ver.
Software Windows Compatible
Accessories Dial Gauge, Weight (4.9 N: 1 pc, 9.8 N: 2 pcs), Hexagon wrench,
Set Up Disk (105-AUTO), Power Plug Adaptor (105-AUTO)
Option Heating Plate Type, Safety Cover
Power Source AC 100 V, 1-Phase, 5 A, 50/60 Hz
Dimensions/Weight (Approx.) W365 × D250 × H500 mm, 15 kg

MCBURNEY INDENTATION TESTER

JIS-A1454, A5705

This tester is to test the indentation of floor material. Adjusting the dial gauge to 0 within 5 seconds after setting an initial load of 9 N, the operator is then to add 133 N of load to the test specimen and read the indentation depth when 1 minute has past.

Spesifikasi

Weight Load Initial 9 N, Total 133 ± 1N
Indenter Hemispherical shape, φ6.35 ± 0.01 mm
Dial Gauge Scale 1/100 mm, Stroke Max. 10 mm
Dimensions/ Weight (Approx.) W180 × D180 × H360 mm, 18 kg

RESIDUAL INDENTATION TESTER

JIS-A1454, A5705

This tester is to test the residual indentation of floor material. The operator is to apply 356 N of load to the specimen for 10 minutes (if the test specimen is foamed material 222 N of load for 5 minutes). After the time has past, remove the load and read the indentation depth of the test specimen when 60 minutes has after the load has been removed.

Spesifikasi

Weight Load 356 ± 1 N, 222 ± 1N
Indenter Standard: Flat shape, φ4.5 mm
Famed Material: Hemispherical shape, φ19 mm
Dial Gauge Scale 1/100 mm, Stroke Max. 10 mm
Option Automatic Loading Device, Timer
Dimensions/ Weight (Approx.) W350 × D350 × H800 mm, 65 kg